Sika ® Injection - 101 RC
Sika ® Injection - 101 RC is a two-component polyurethane, for low viscosity fast sparkling water reactive perfusion resin, can be solidified into a soft foam density.
- Foam reaction occurs only in direct contact with water
- A single set of subsystem of perfusion
- Free foaming expansion up to 40 times
- At low temperature (< + 10 ° C) use Sika ® Injection - AC10 acceleration
Using range
- Concrete and masonry cracks, seams, and gaps in temporary water high pressure water intrusion
- Special construction of water, such as drilling or steel sheet pile wall, anchor head and micro channel
- In order to achieve a permanent waterproof fissure sealing, can be used after the temporary water stop Sika ® Injection - 201 CE or Sika ® Injection - 203
Feature/advantages
- Foam reaction occurs only in direct contact with water
- A single set of subsystem of perfusion
- Free foaming expansion up to 40 times
- At low temperature (< + 10 ° C) use Sika ® Injection - AC10 acceleration
packaging
| A agent (resin) | 10/20 kg |
| B agent (hardener) | 12.5/25 kg |
Please refer to the packing list
color
| A agent (resin) | Colorless, |
| B agent (hardener) | brown |
Technical information
Environmental information
- FEICA environmental product declaration (EPD)
Certification/standard
For the federal transit route ZTV - ING structure and component of polyurethane and perfusion project assembly, part 3, section 5 (RISS), Sika ® Injection - 101 RC, Bundesanstalt fur Strassenwesen, 20.01.2016
- According to the KTW suggested widespread applicability, sealant Sika ® Injection - 101 RC, LADR Zentrallabor, July 2019
Chemical composition
Water-based polyurethane resin reaction
The best life
Since the production date 24 months
Storage conditions
Products to original preservation in + 5 ° C to + 35 ° C in the dry environment.Please refer to the packing instructions.
The density of
| A agent (resin) | About 1.0 kg/l |
| B agent (hardener) | About 1.25 kg/l |
Measured data from + 20 ° C
viscosity
A agent (resin) |
About 140 mPa, s |
B agent (hardener) |
About 155 mPa, s |
Measured data from + 20 ° C
Inflation rate
| Inflation began to | About 15 seconds after contact with water |
| All over | About 67 seconds |
Measured data from + 20 ° C
applied
Mix proportion
Agent A agent: B = 1:1 by volume)
The reaction time
(10081-11 PM)
| 0% Sika ® Injection - AC10* | ||
| Material temperature | Inflation began to |
All over |
| + 5 ° C | About 19 seconds | About 89 seconds |
+ 10 ° C |
About 17 seconds |
About 88 seconds |
+ 20 ° C |
About 16 seconds |
About 70 seconds |
| 5% Sika ® Injection - AC10* | ||
| Material temperature | Inflation began to | All over |
| + 5 ° C | About 12 seconds | About 57 seconds |
| + 10 ° C | About 11 seconds | About 49 seconds |
+ 20 ° C |
About 10 seconds | About 39 seconds |
| 10% Sika ® Injection - AC10* | ||
Material temperature |
Inflation began to | All over |
| + 5 ° C | About 9 seconds | About 41 seconds |
+ 10 ° C |
About eight seconds | About 37 seconds |
+ 20 ° C |
About 7 seconds | About 35 seconds |
* Sika ® Injection - AC10 dosage for Sika ® Injection - 101 RC (A + B) % of the weight
Data for the laboratory parameters, probably because of the actual case in field condition
The reaction rate (foam molding) will be mixed material temperature, structure and contact with moisture, and fluid mechanics
Smaller volume usage can adopt A agent: B = 1:1 volume
Environmental atmospheric temperature
Minimum + 5 ° C/h + 35 ° C
Element to temperature
Minimum + 5 ° C/h + 35 ° C
Operating time
About two hours (in + 20 ° C) |
(ISO 9514). |
hybrid
Add A + B agent into the mixing vessel, slow thoroughly mix (maximum 250 RPM) at least 3 minutes, until just combined
After mixing, the material in container of feed pump, a little stirring and used in the use of time
If the base material and/or environmental temperature < + 10 ° C, can be Sika ® Injection - AC10 added to the Sika ® Injection - 101 RC, to speed up the expansion
Tools to clean
Use Sika ® Injection system to clean all the tools and construction equipment